سفارش تبلیغ
صبا

مقاله Hydroxyapatite/Titania Nanostructure Biocoating on Ti6Al4V

 

برای دریافت پروژه اینجا کلیک کنید

مقاله Hydroxyapatite/Titania Nanostructure Biocoating on Ti6Al4V Alloy by SolدرGel DipدرCoating فایل ورد (word) دارای 3 صفحه می باشد و دارای تنظیمات در microsoft word می باشد و آماده پرینت یا چاپ است

فایل ورد مقاله Hydroxyapatite/Titania Nanostructure Biocoating on Ti6Al4V Alloy by SolدرGel DipدرCoating فایل ورد (word) کاملا فرمت بندی و تنظیم شده در استاندارد دانشگاه و مراکز دولتی می باشد.

این پروژه توسط مرکز مرکز پروژه های دانشجویی آماده و تنظیم شده است

توجه : در صورت  مشاهده  بهم ریختگی احتمالی در متون زیر ،دلیل ان کپی کردن این مطالب از داخل فایل ورد می باشد و در فایل اصلی مقاله Hydroxyapatite/Titania Nanostructure Biocoating on Ti6Al4V Alloy by SolدرGel DipدرCoating فایل ورد (word) ،به هیچ وجه بهم ریختگی وجود ندارد


بخشی از متن مقاله Hydroxyapatite/Titania Nanostructure Biocoating on Ti6Al4V Alloy by SolدرGel DipدرCoating فایل ورد (word) :

سال انتشار: 1388

محل انتشار: سومین کنفرانس نانوساختارها

تعداد صفحات: 3

چکیده:

The aim of this work is to produce hydroxyapatite (HA) coatings on titanium alloys (Ti6Al4V) for facilitating and shortening the processes towards osseointegration. The TiO2 layer was inserted between Ti6Al4V substrate and HA coating to improve the corrosion resistance of substrate as well as bonding strength between metal substrate and ceramic coating. TiO2 and HA coatings were obtained by sol–gel dip-coating. After preparing of
substrates, they dipped into TiO2 sol, and this followed by heat- treatment at different temperatures. Calcination at 400°C for 1h was chosen as optimum condition for heat treatment of TiO2 coatings. Subsequently, the HA layer was coated and heat treated at 350°C for 30 min. X-ray diffraction (XRD) analysis were used to study the phase composition of coatings. Morphology of coatings was also performed using a scanning electron microscope (SEM). The corrosion resistance of samples was assessed by polarization test under simulated body fluid (SBF) at 37°C. The bioactivity of sol–gel coatings was observed during soaking of them inside SBF at 37 °C for 28 days.

 

 